BIOCOMPATIBILIDADE DE IMPLANTES PRODUZIDOS POR PROTOTIPAGEM RÁPIDA DE ACRILONITRILA BUTADIENO ESTIRENO (ABS) E POLIAMIDA EM FÊMURES DE COELHOS
JOAO VICTOR ROMANO VIEIRA
DISSERTAÇÃO
30/01/2017

O objetivo deste estudo foi avaliar a eficiência da osteointegração, biocompatibilidade e osteocondução dos implantes de ABS (acrilonitrila butadieno estireno) e poliamida confeccionados por prototipagem rápida, com canais de interconexões, aplicados em região intraóssea de fêmures de 12 coelhos. Foram realizadas perfurações nos sulcos trocleares esquerdo e direito com diâmetros de 5mm para aplicação dos implantes de ABS (esquerdo) e poliamida (direito) e os animais foram avaliados clínica e radiograficamente aos 15, 30, 45 e 90 dias. Após cada período de avaliação todos os animais foram eutanasiados e as porções distais dos fêmures foram colhidas para avaliação histopatológica. Nas avaliações radiográficas não foi possível a visibilização dos implantes nos períodos de avaliação. Observaram-se pequenas áreas escleróticas em sobreposição ao defeito ósseo em epífise e diáfise aos 30 dias, e aspectos ósseos semelhantes ao do fêmur distal normal aos 90 dias em ambos os implantes. Macroscopicamente identificou-se integração entre osso-implante para os dois materiais a partir dos 15 dias. Histologicamente aos 90 dias a cavidade do implante apresentava-se preenchida com matriz óssea madura, sem reação inflamatória no ABS, porém, intensa atividade magrofágica e resíduos de células gigantes foram evidenciados na poliamida. Os implantes mostraram-se biocompatíveis e osteocondutores, com integração osso-implante, contudo o ABS foi superior comparativamente à poliamida por apresentar menor atividade inflamatória no decorrer do processo de avaliação.

biomateriais;osso;implantes;defeito;reconstrução óssea
The aim of this study was to evaluate the efficiency of osseointegration, biocompatibility and osteoconductive properties of ABS (acrylonitrile butadiene styrene) and polyamide implants made by rapid prototyping, with interconnections channels applied Intraosseous region of the femur in 12 rabbits femurs. Drillings of 5mm diameter on the left and right trochlear grooves for application of ABS (left) and polyamide (right) implants were carried out. At 15, 30, 45 and 90 days, the animals were clinically and radiographically evaluated. After each evaluation period, all animals were euthanized and the distal portions of femurs were fixed for histological evaluation. In the radiographic evaluation was not possible the visualization of the implants in the evaluation periods. At day 30, small areas superimposed the sclerotic bone diaphysis was seen, and at 90 days, epiphysis defect and bone aspects similar to the normal knee were observed in both implants. After 30 days macroscopically was identified integration between the bone-implant for the two materials. Histologically at 90 days, in the ABS, the implant well was filled with mature bone matrix without inflammatory reaction, and intense macrophages activity and giant cells residues were evidenced in polyamide. The implants proved to be biocompatible and osteoconductive, with bone-implant integration, however the ABS presented less inflammatory activity during the evaluation process to the polyamide to present.
biomaterials;bone;implants;defect;reconstruction
01
74
PORTUGUES
UNIVERSIDADE FEDERAL DA BAHIA
O trabalho possui divulgação autorizada

Contexto

SAÚDE ANIMAL
PATOLOGIA, CLÍNICA E CIRURGIA VETERINÁRIA
AVALIAÇÃO DE BIOMATERIAIS NA MEDICINA VETERINÁRIA

Banca Examinadora

ARIANNE PONTES ORIA
DOCENTE - PERMANENTE
Sim
Nome Categoria
TIAGO DA CUNHA PEIXOTO Docente - PERMANENTE
JOAO MOREIRA DA COSTA NETO Docente - PERMANENTE
ARIANNE PONTES ORIA Docente - PERMANENTE
NATALIE BORGES LEITE Participante Externo

Financiadores

Financiador - Programa Fomento Número de Meses
CONS NAC DE DESENVOLVIMENTO CIENTIFICO E TECNOLOGICO - CAPES 24

Vínculo

CLT
Empresa Privada
Ensino e Pesquisa
Sim