ESTUDO DE CONCRETO ARMADO COM FIBRAS PARA BLINDAGEM DE ESTRUTURAS PARA DEFESA
RENATO CANCHERINI LEFONE
DISSERTAÇÃO
26/02/2014

Este trabalho tem por objetivo estudar o comportamento de placas de concreto armado de alta resistência, reforçadas internamente com fibras de aço e externamente com tecido de material compósito de fibras de vidro, quando submetidas a impactos balísticos. Para tal, executou-se um programa experimental com 56 placas quadradas de 30 cm de dimensão. Os parâmetros experimentais variáveis foram: a espessura das placas (70 mm,100 mm,125 mm e 150 mm), a resistência à compressão do concreto (fc = 70 e 90 MPa), a curvatura da face de ataque (uma face plana e três faces curvas), o reforço externo de GFRP, o calibre do projétil (7,62 mm e 12,7 mm), o tipo da munição (comum ou perfurante), e a velocidade de impacto do projétil (823,0 m/s a 905,82 m/s). Disparou-se apenas um tiro na região central de cada placa, com ângulo de impacto de 90o. Concluiu-se que cada tipo de projétil utilizado foi contido com uma das configurações de placa de concreto definidas no programa experimental. Mostrouse, assim, a utilidade do trabalho no desenvolvimento de um concreto armado capaz de manter a estabilidade e integridade das edificações, quando submetidas a impactos balísticos.

1. Engenharia de defesa – teses e dissertações. 2. Construção. 3. Concreto armado. 4. Fibras de aço.
This study aims the experimental analysis of the ballistic impact resistance of steel fibers reinforced high strength concrete plates, reinforced externally by GFRP fabric. 56 square plates with dimensions of 30 cm x 30 cm were casted. The variable experimental parameters were: thickness of the plates (70 mm, 100 mm, 125 mm and 150 mm), concrete compressive strength (fc =70 MPa and fc = 90 MPa), curvature of the attack face (one flat face and two different curved faces), rate of steel reinforcement, GFRP reinforcement, caliber of the projectile (7,62 mm and 12,7 mm), type of ammunition (common or perforator) and impact velocity of the projectile (823,0 m/s to 905,82 m/s). One shot was fired on the target center of each plate, with 90 degrees impact angle. It was concluded that each type of projectile was resisted by one of the concrete plate configuration defined in the experimental program. So, the usefulness of the work in the development of a special concrete to resist ballistic impact, has been showed.
1. Defense Engineering Course (Thesis and dissertations). 2. Concrete. 3. Steel fiber
1
230
PORTUGUES
INSTITUTO MILITAR DE ENGENHARIA
O trabalho possui divulgação autorizada

Contexto

ENGENHARIA DE DEFESA
MODELAGEM E SIMULAÇÃO EM SISTEMAS DE DEFESA
Estruturas para infraestrutura de transportes e de defesa

Banca Examinadora

LUIZ ANTONIO VIEIRA CARNEIRO
DOCENTE - COLABORADOR
Sim
Nome Categoria
ALAELSON VIEIRA GOMES Participante Externo
EMIL DE SOUZA SANCHEZ FILHO Participante Externo

Vínculo

Servidor Público
Instituição de Ensino e Pesquisa
Ensino e Pesquisa
Sim