DESENVOLVIMENTO E CARACTERIZAÇÃO DE MEMBRANAS ELETROFIADAS A BASE DE BORRACHA NATURAL E POLI(ε -CAPROLACTONA)
LIGIA MARIA MANZINE COSTA
TESE
11/02/2014

Neste trabalho foram desenvolvidas e caracterizadas membranas eletrofiadas de poli(ε-caprolactona) e borracha natural (PCL/BN). O objetivo foi a obtenção de novos biomateriais nanoestruturados utilizando uma matéria-prima nacional. Para isso inicialmente foram realizados estudos dos parâmetros de processamento por eletrofiação para o PCL. Após a obtenção dos parâmetros de processamento para o PCL, foram introduzidas porções de BN dissolvida em tolueno nas soluções a serem eletrofiadas. As membranas foram caracterizadas morfologicamente por microscopia eletrônica de varredura (MEV). Os grupos funcionais das moléculas presentes no material foram analisados por espectroscopia de infravermelho por transformada de Fourier (FTIR). As membranas também foram caracterizadas termicamente por análise calorimetria exploratória diferencial (DSC) e por análise termogravimétrica (TGA), e avaliado os comportamentos mecânicos através de curvas de tensão verso deformação extraída de um analisador dinâmico mecânico (DMA). Foram ainda realizados ensaio da gota séssil para verificar a molhabilidade do material e ensaios qualitativos e quantitativos de citotoxicidade in vitro das blendas eletrofiadas. Os resultados demonstraram a criação de um material nanoestruturado com alta porosidade e altamente elástico, além de possuir resistência mecânica, não ser citotóxico e possuir molhabilidade, podendo ser utilizado em aplicações como “scaffols” em engenharia de tecidos, sistemas de liberação de fármacos, sistemas de filtração, sensores bioquímicos após funcionalização, entre outras.

Borracha natural, poli(ε-caprolactona), nanofibras, eletrofiação
In this work, it was developed and characterized PCL/natural rubber electrospun mats. This work aim to obtain new nanostructured biomaterials with natural materials from brazilian environment. Initially, it was studied processing parameters from PCL electrospun. After, it was added natural rubber in PCL solubilized samples for electrospinning. Electrospun mats samples were morphologically characterized by SEM (scanning electron microscope) and functional groups were characterized by FTIR (fourier transform infrared spectroscopy). Thermal behavior of Natural rubber/PCL electrospun mats were characterized by TGA (thermogravimetric analysis) and DSC (differential scanning calorimetry) besides mechanical properties were characterized by stress- strain curve using DMA (dynamic mechanical analysis). wettability behavior were studied by sessile drop and qualitative and quantitative in vitro citotoxicity analysis were perfomed. Results showed nanostructured material with high porosity, thermal properties, mechanical properties, wettability properties and without citotoxicity with application in tissue engineering, drug delivery, filtration and sensors.
Natural rubber, poly(ε - caprolactone), nanofibers, electrospinning
1
135
PORTUGUES
UFABC

Contexto
NANOCIÊNCIAS E MATERIAIS AVANÇADOS
POLÍMEROS
-

Banca Examinadora
Orientador:
MARISELMA FERREIRA
O orientador principal compôs a banca do discente?
Sim
Nome Categoria
JOSE ANTONIO MALMONGE Participante Externo
CHRISTIANE BERTACHINI LOMBELLO Participante Externo
RAFAEL SALOMAO Docente
DANILO JUSTINO CARASTAN Docente


Vínculo
-
-
-
Não
Setor Bancário Norte, Quadra 2, Bloco L, Lote 06,
CEP 70040-020 - Brasília, DF CNPJ 00889834/0001-08 -
Copyright 2010 Capes. Todos os direitos reservados.
Desenvolvido pela Cooperação CAPES e SINFO